Assessing the Effect of Different Mortar Mixes on Strength of Burnt Clay Brick Masonry Wall

DOI : 10.17577/IJERTV9IS050182

Download Full-Text PDF Cite this Publication

Text Only Version

Assessing the Effect of Different Mortar Mixes on Strength of Burnt Clay Brick Masonry Wall

Owino Stephen, Dr. Kyakula Michael, Dr. Mugume Rodgers Bangi Faculty of Engineering, Department of Civil and Building Engineering, Kyambogo University, Uganda.

Abstract :The population of Uganda grew from 12.6m in 1980 to 34.6m in 2014. This has been matched by an increase in housing demand. The estimated annual demand is 200,000 units per year. The National Housing and population census of 2014 showed that burnt clay bricks are the most commonly used walling material at 36.4% followed by mud and poles at 33.6%. However, there is no data on the strength of burnt clay brick walls and the relationship between strength of bricks and that of mortar that would inform design. A survey of 24 Structural Engineering consultancy firms was carried and it was found that none of these design masonry walls made from burnt clay bricks. A survey of 102 sites revealed that the batching method employed was a bag of cement to a number of wheelbarrows. Thus a mix of one bag of cement to three wheel barrows would be specified as 1:3, yet the average volume of a wheel barrow is about 0.089m3 and the volume of a 50Kg bag of cement is about 0.036m3. Tests revealed that the water absorption of the bricks varied from 9.23% to 16.68%. The strength of the bricks varied widely from 1.62N/mm2 to 8.49N/mm2. The source of sand used on most sites determined the source of sand used in making mortar cubes. The strength of mortar cubes varied from 17.8N/mm2 at 1:3 to 1.87N/mm2 at 1:14. Masonry walls of 1m wide by 1m high were constructed with mortar mixes to match those in the field and the walls were tested under compression. Tests revealed that mortar joints fail before bricks. The strength of the wall constructed varied from 1.85N/mm2 at 1:7 mortar mix to 1.49N/mm2 at 1:14 mortar mix. This was 69% to 77% of the designed wall strength. The failure of the mortar before bricks eases maintenance because mortar is more flexible and cracks in mortar tend to be smaller and easier to repair.

Key Words : Mortar mixes, Mortar Cube strength, Brick strength and Wall strength

  1. INTRODUCTION TO THE STUDY

    There has been a tremendous increase in Ugandas population growth rate from 1.2% in 1980 to 3% in 2014 leading to a population of 34.6 million people in 2014 from

    12.6 million people in 1980, (UBOS). This has been characterized by growth in housing units from 2.6 million houses in 1980 to 7.34 million houses in 2014 with 75% of the population leaving in rural areas and 25% urban dwellers. The forecast showed an increase in population to 47 million people in 2025 and 63 million people in 2040 indicating an increase in demand of housing units to cater for the increased population, (UBOS, 2014). The estimated annual housing demand is 200,000 units per year. The 2014 housing and population census showed that houses with permanent walling materials constituted 43.7%. It further showed that burnt clay brick walls were the most used walling material at 36.4% followed by mud and poles at

    33.6% as given in distribution of Household Walling Materials, (UBOS, 2014).

    The purpose of cement in the mix of cement-lime – sand mortar is to unite coarse grained sand particles together, (Clark Deichler, 1936). The use of cement as a binder has greatly increased from 1.37 billion tons in 1994 to 3.7 billion tons in 2012, (Zainab Hashim Abbas, 2017). The evaluation of the mechanical properties of mortar by (Marcos Venicus, et.al., 2014), indicated that cement – sand mortar is flexible, easy to work with and easy to repair. Hamid Eskandari (2017), revealed that the strength of mortar increased with age and depends on the class of cement. Francis M.Fernandes, (2009), found out that ordinary clay bricks were difficult to characterize due to the wide diversity of raw materials and the manufacturing process. Results revealed scattering compressive strength ranging between 1.5- 30 MPa and this depended mostly on the water absorption rate of the burnt clay bricks. Konthesingha.C, (1985), investigated the effect of bond strength and compressive strength of ordinary clay bricks and standard bricks. Results revealed that standard bricks gave a higher tensile and shear strength compared to ordinary bricks and hence good bondage is evidenced with use of standard bricks engineered bricks''. Mosalam, et.al., (2009), found out that the interface between mortar and masonry units is the weakest link in the system and this depended entirely on properties and composition of the constituents.

    Nassif Nazeer, (2018), revealed that the strength of masonry structures entirely depends on the thickness of the bed joint, height to thickness ratio in relation to mortar strength. Emeritus and Hendry, (2001), reviewed different types of masonry walls among which included those constructed of burnt clay bricks, concrete blocks and calcium silicate bricks where clay burnt masonry structures revealed a strength of about 100MPa for commercial buildings and between 20 – 40MPa for domestic buildings and 2.8 – 35MPa for concrete block structures.

    This research was therefore set out to determine the mortar mix ratios used on construction sites around Kampala and to determine the mortar strength corresponding to mortar mix ratios commonly used around Kampala. It also sought to determine the strength of bricks used on sites around Kampala and thus establish strength of the wall in relation to mix ratios, brick strength and mortar strength

  2. METHODOLOGY

      1. Materials tested

        This research investigation, the following materials were tested in the assessment of the effect of different mortar ratios on the strength of burnt clay masonry walls

        • Fine grained sand

        • Course grained sand

        • Mortar cubes

        • Burnt clay bricks and

        • Brick walls 1m long x 1m high x 0.2m wide

      2. Tests carried out

        The following tests were carried out to ascertain the quality of the materials that were used in the construction of burnt clay brick masonry walls.

        • Sieve analysis test on the sand samples

        • Specific gravity and bulk density of the sand samples

        • Water absorption on bricks

        • Compressive strength of the mortar cubes

        • Compressive strength of burnt clay bricks

        • Compressive strength of the masonry wall structures

  3. RESULTS

Mortar mixes

Table 1, Shows the mortar mixes used on 102 site

Table 1, shows that 46% of the sampled sites uses one bag of cement of 50Kg to four wheel barrows full of sand,(1:4), 32% of the sites uses one bag of cement of 50Kg to five wheelbarrows full of sand, (1:5), 16% uses one bag of cement of 50Kg to six wheel barrows full of sand, (1:6), 6% uses one bag of cement to three wheel arrows full of sand, (1:3) and 1% uses one bag of cement to two wheelbarrows full of sand, (1:2).

  1. Of the 102 sites surveyed it was found that 76 sites used mortar mix proportions dictated by the site engineer while 26 sites revealed that this is dictated by the client.

  2. All the 102 sites revealed that they use cement: sand mortar. The mortar ratios used on the 102 sites are given in Table 1.

  3. The batching methods used on all 102 sites was number of cement bags to number of full wheelbarrows of sand.

  4. The volume of a 50Kg bag of sand was found to be 0.036m3. And the average volume of different wheelbarrows used on 102 sites was 0.089m3 when

    filled to he top of the wheelbarrow bucket as shown in Figure 1.

  5. The level to which a wheel barrow is filled depended on the whims of workforce or the supervisors. There was no site where guidelines on the level of filling the wheel barrow was found. All sites revealed that the sand was heaped above the top of the wheel barrow bowel as shown in Figure 1.

  6. One bag of cement to three wheel barrows of sand is not actually 1:3 as the site engineers assessment but 1: (3*2.47) = : 7.42 , therefore tests carried out in this work used the commonly field observed mix proportion.

  7. The mix proportions used in the field are not appropriate to the strength intended since a wheel barrow of sand media is 2.47 times the volume of a cement bag.

  8. 59% of the sites indicated that they mix fine sand and coarse sand to make the sand media in the mortar, 32% of the sites use only coarse sand and 7% use only fine sand. Because 59% of the 102 sites use a combination of fine and coarse sand, the experiments were designed to use the same.

  9. Results of compressive strength of trial tests on individual mortar obtained from a mix of a single type of sand revealed that compressive strength of obtained from single sand type mixed with cement varied much with no consistency while results of the mix of the two sand type mixed with cement indicated consistency in the results as shown in Figure:2.

Figure 1 : Wheel barrow full of sand and wheelbarrow of cement (50 kg bag cement)

Figure: 2, shows a graph of compressive strength of mortar Vs mix proportions

Sand media used

On all 102 sites the respondents explained that the site engineer determined the source of sand based on experience. Research found out that 59% of the sites around Kampala used coarse sand extracted from Rwera mining site along Kampala – Masaka road and this was followed by Buwama sand at 16%, Kapeeka sand at 12% and lastly Lake Victoria and Kamengo at 7%.

  1. Sieve analysis test on coarse grained sand

    The sand for use in construction industry should meet the requirements with respect to grading, absence of organic matter and absence of excessive clay, according ASTM C136/C136M. Rwera sand was chosen to be used in this experiment because it is the most used sand. Figure:3, shows the results of the sieve analysis tests carried out on sand from Rwera mining site. Results revealed that the sand is well graded.

    Gradation curves for coarse grained sand

    Figure : 3, Gradation curve for coarse grained sand

  2. . Sieve analysis test of fine grained sand

    A survey of 102 sites revealed varying sources of fine grained sand (locally called plaster sand) depending on the location of the site. This sand is usually extracted from the nearest valley to the sites. Considering Kampala Jinja road, 9 sites of the fifteen sample size used fine grained sand from Katosi, hence, its selection for use in this experiment. The results of the sieve analysis in Figure:4

    Gradation curves for fine grained sand

    Figure: 4,Gradation curve for fine sand

  3. Specific gravity test and bulk density test on sand media used

    The results for specific gravity of the sand media was determined using pyconometer method in accordance with ASTM C 127-1993 and the bulk density test which was conducted in accordance to BS 812-2 (1995). Results from specific gravity test revealed that specific gravity for coarse grained sand is 2.73 and that of fine grained sand is 2.61. This is within the range specified by IS : 2386 ( Part III )

  4. Cement

    The type of cement used on sites varied from site to site depending on the availability on the local market; this research found that 56% of the sites use 32.5R and 44% use 32.5N.

  5. Compressive strength of mortar Cubes

    In accordance to ASTM C109/C109M standard method for testing the compressive strength of cement mortar, a total of 36 mortar cubes were tested after 28 days of curing and their compressive strength recorded, these comprised of mortar ratios from 1:3, 1:4, 1:5, 1:6, 1:7, 1:8, 1:9, 1:10,

    1:11, 1:12, 1:13 and 1:14, mortar ratios from 1:7 to 1:14 represented the commonly used corrected field mix proportions.

    Figure: 5, Compressive strength of mortar cubes

    From Figure:5, the commonly used field observed mortar ratios are found to have a maximum strength of 6.82N/mm2 at mix proportion 1:7 and a minimum strength of 1.87N/mm2 at a mix proportion of 1:14. From field evaluation of batching methods, mix ratios less than 1:7 were not used.

  6. Bricks

    In this research study, burnt clay bricks from Hoima road were used due to its good properties and relatively moderate deviation in compressive strength.

    1. Compressive strength of burnt clay bricks Results of compressive strength of bricks sourced from 35 construction sites along major roads joining Kampala metropolitan among showed that the average compressive strength of burnt clay bricks varied from 9.7N/mm2 to 1.6N/mm2

      Table 2: Summary of the average compressive strength of burnt clay bricks from the major selected bricks

      Table 2: Average compressive strength of burnt clay bricks

      MAJOR ROADS

      A1

      A2

      A3

      A4

      A5

      Hoima road

      8.5

      8.1

      7.6

      6.3

      4.5

      Mityana road

      1.7

      2.1

      2.3

      2.5

      3.2

      Gayaza road

      6.2

      3.8

      3.6

      4.6

      4.6

      Bombo road

      2.9

      2.9

      2.8

      2.5

      2.9

      Masaka road

      5.3

      9.1

      9.7

      8.8

      3.7

      Entebbe road

      2.3

      1.6

      2.7

      2.2

      1.6

      Jinja road

      5.5

      3.7

      6.1

      2.8

      4.3

      Figure :6, Compression test of burnt clay bricks

    2. Variability of compressive strength of burnt clay bricks

      Using the statistical method of validating the variability of materials, it was found out that materials used around Kampala vary widely in compressive strength. Masaka

      road bricks had the highest deviation of 3.21N/mm2, followed by Gayaza road with 2.49N/mm2, Hoima road with 1.73N/mm2, Jinja road with 1.60N/mm2, Bombo road with 1.20N/mm2, Mityana road with 0.93N/mm2 and finally Entebbe road with 0.65N/mm2, this is clearly indicated in Figure: 7.

      3.21

      1.73

      3.21

      1.73

      – .00

      – .00

      Major roads

      Major roads

      Standard deviation in compressive

      Standard deviation in compressive

      12.00

      10.00

      12.00

      10.00

      8.00

      8.00

      6.00

      6.00

      2.49

      2.49

      1.6

      1.6

      4.00

      4.00

      7.30

      7.30

      7.00

      7.00

      1.2

      1.2

      2.00

      2.00

      4.56

      4.56

      4.46

      4.46

      0.93

      0.93

      2.79

      2.79

      2.34

      2.34

      0.65

      2.06

      0.65

      2.06

      Compressive strength, N/mm2

      Compressive strength, N/mm2

      Figure 7: Summary of availability of compressive strength of bricks around Kampala

    3. Relationship between water absorption and Compressive strength of burnt clay bricks

      From Figure 8:, test results revealed that higher percentage of water absorption results into low compressive strength.

      Figure 8: Relationship between water absorption and Compressive strength of burnt clay bricks

  7. <2>Determination of masonry wall strength using the test results obtained from the Laboratory

    According to EN BS 1996-1-1:2005, the compressive strength of a wall is given by

    f Kf 0.7 f 0.3

    (1.0)

    k b m

    Where;

    f k is the characteristic compressive strength of

    masonry wall in N/mm2

    K is a constant based on the group number and

    type of mortar, Table3.3, EN1996.1.1:2005

    fb is normalized mean compressive strength of

    the masonry units used.

    N/mm2

    f m is the compressive strength of mortar in

    The normalized mean compressive strength is given

    by

    fb = [conditioning factor] * [Shape factor] * [

    Declared mean compressive strength]

    Declared mean compressive strength is obtained from experimental data

    For air dried bricks, conditioning factor is 1.0, EN

    772-1.

    Figure 9: The compressive strength of masonry walls

    Figure 9:, it is seen that when weak bricks are used with high strength mortar, the strength of the wall is found to be influenced more by the weak bricks strength. Whereas from from Table 4.4, the mortar strength varies from 17.8N/mm2 for 1:3 mix ratio to 1.87N/mm2 for 1:14N/mm2 mortar ratio. The strength of the wall is considerably reduced to vary from 3.9N/mm2 for 1:3 mix ratios to 0.82N/mm2 at 1:14 mix ratio.

  8. Determination of wall compressive strength constructed of field derived mortar ratios

A set of twelve walls were constructed using mortar mixes 1:7, 1:10, 1:12 and 1:14 for each of the tests. The ratios were obtained after a field survey that revealed an average volume of a wheel barrow to be 0.089m3 and the volume of a cement bag of 0.036m3 thus these ratios were the most applicable in the field. These were tested after 28 days using a steel loading machine at Kireka materials laboratory

Figure 10: Wall structure (1000 x 1000) mm tested and failure of the walls)

100% of the tested walls failed due to the effect of a weaker bond strength between bricks and mortar this was evidenced by the crack patterns that followed the mortar joints with less cracks through the bricks as shown in Figure 10 indicating a failure due to bond effect.

Table 3: Relationship between tested wall strength and designed wall strength

From the Table 3, its observed that the compressive strength of tested walls reduced with increasing value of mix ratios as was expected. Tested results varied from 68% to 77% of the calculated designed strength of the wall.

From Figure 12, it is seen that the lowest average brick strength is 4.7N/mm2, this resulted into wall strength of 1.43N/mm2 and the highest brick strength is 11.73N/mm2 resulting into a wall strength of 2.15N/mm2. Thus an increase in brick strength of 150% resulted into only 50% effect of brick strength and the wall strength is not so much pronounced.

k) Load capacity for walls and implication factor for design

For a wall (200mm wide x 4000mm long) of mortar mix (1:14) and average brick strength of 7.0N/mm2. This would be able to support 1,192 KN.

Compressive strength =

LoadKN

Contactarea

……..(2)

Figure 11: Tested wall strength vs designed wall strength

Table 4: Wall strength constructed of different mortar ratios

The load capacity is ( 200 x 4000 x 1.49) x 10-3 = 1.192KN It would be wrong for an Engineer to ignore this load carrying capacity and instead use bricks as infill. Exploiting the load capacity of the wall would serve as a factor of safety against differential settlements due to disturbed soils. It would ensure that the wall serves as a fuse during seismic loading.

Hence Design wall resistance,

N Rd

f k t

……….

…….( 3 )

0 . 68

m

1 . 49

1 . 0

200

10 3

0 . 203 KN / m

Table 4, shows the different wall strength obtained from wall units constructed of different mortar ratios using bricks of varying compressive strength, 3 samples of bricks were picked from the materials for each walling unit before construction of the unit. They were tested for compressive strength and the average found.

2.20

2.10

Wall Strength, N/mm2

Wall Strength, N/mm2

2.00

1.90

1.80

1.70

1.60

1.50

1.40

1.30

4 6 8 10 12

Brick Strength, N/mm2

Wall in (1:7) Wall in (1:10)

Wall in (1:12) Wall in ( 1:14)

Figure: 12, Relationship between wall strength and brick strength

4.1 CONCLUSION DRAWN FROM THE THESIS

  • The actual mortar mixes used on construction sites in Kampala (Uganda) have been found to be 1:7, 1:10, 1:12 and 1:14 and not the perceived mix ratios of 1:3, 1:4, 1:5 and 1:6, this is due to use of un calibrated

    batch methods of using a 50Kg bag of cement to a number of wheel barrows yet their volumes are not equal.

  • The strength of bricks used on constructions in Kampala (Uganda) varied greatly from 9.7N/mm2, 1.6N/mm2 averagely. This means in design the lowest strength is applicable .

  • The compressive strength of mortar mix ratios used on construction sites was found to be 5.92N/mm2 for

    1:7, 3.04N/mm2 for 1:10, 2.49N/mm2 for 1:12 and 1.87N/mm2 for 1:14. This is safe design since the bricks strength used varied from 7.0N/mm2 to 2.06N/mm2 . And the strength of mortar should not be greater than the strength of bricks because mortar is more flexible and cracks in mortar are easy to repair.

    Additionally the strength of the chain is determined by its weakest link. Thus if two materials are used it is proper and economical Engineering if their strength does not vary much.

  • The average strength of walls tested varied from 1.85N/mm2 to 1.49N/mm2 averagely for mortar ratios 1:7 and 1:14 respectively. The average compressive strength of bricks used varied from 11.71N/mm2 to

4.67N/mm2. The resultant wall strength was much influenced by the strength of mortar, indicating that the weaker the strength of mortar the weaker the wall strength however strong the bricks may be. So, in construction the strength of mortar is key in determining the strength of the wall.

4.2 RECOMMENDATIONS

From the test data observations, the following recommendations have been made to support both academic and construction industry in Uganda.

  1. The construction industry in Uganda should employ proper batching methods like the use of batch boxes as a way of ascertaining the actual mortar mixes used and thus improving on the durability and strength of masonry walls.

  2. The construction industry should always determine the water absorption and compressive strength of masonry units during design and construction as this affects the strength of a masonry wall.

  3. Structural design firms should always design masonry walls made of burnt clay bricks as load bearing walls other than providing them as infills to reduce on cost of construction, and to utilize all materials in carrying loads.

ACKNOWLEDGEMENT.

I would like to thank my supervisors, Dr. Kyakula Michael, Dr. Mugume Rogers Bangi,

My course-mates Eng.Nsubuga Jacob and Madete Robert , Kireka Materials Central Laboratory Uganda and UNRA Material Laboratory Kyambogo branch for their pecious time in reading , guidance and financial assistance given throughout this research work may God bless you abundantly.

  1. NIVETHA C, J. D. R. L., 2017. Study on strength and behaviour of red mud bricks. Jr. of Industrial Pollution Control

    , Issue 33, pp. 1227-1230.

  2. Office, U. G. P., 1961. effect of Mortar Properties on the strength of Masonry. 20 ed. US Washington: Cyrus c.fishburn.

  3. Stephen Zsembry, G. A. a. T. M., 1982 – 2002. Determining the compressive strength of Clay bricks. C.B.P.I, pp. 308-320.

  4. Thanikasalapradeep Nagarajan, S. V. R. V. a. P. N., 2014. Experimental Approach to Investigate the Behaviour of Brick Masonry for Different Mortars Ratios. International Conference on Advances in Eingineering and Technolohy, pp. 29-30.

    5.1 REFERENCES

    1. K.Mosalam,|L.Glascoe,J.Bemier.,2009. Mechanical Properties of Unreinforced Brick Masonry , Issue 10, pp. 7-8.

    2. Farraj Al – Ajmi, H. A. A. A. J. A., 2016. Strength Behavior of Mud Brick in Building Construction. Open Journal of Civil Engineering, Issue 6, pp. 482-494.

    3. Francisco M.Fernandes, P. B. a. F. C., 2009. Ancient Clay Bricks:Manufacture and Properties. ISISe, civil engineers Department, pp. 1-17.

    4. Hamid Eskandari – Naddaf, R. K., 2018. Experimental evaluation of the effect of Mix design on compressive strength of cement mortars containing cement strength class 42.5 and 52.5MPa. ScienceDirect, Issue 22, pp. 392-398.

    5. Julian Thamboo, N. J. B., 2019. Characterization and Mix specification of commonly used mortars. Research article.

    6. K.M.C Konthesingha, C. a. S., 2007. Bond and Compressive Strength of Masonry for Locally Available Bricks. The Institution of Engineers,Sri Lanka, XXXX(04), pp. 7-13.

    7. Khwairakpam sachidananda, W. V. J. s. S. L., 2017. characteristic Strength of Machine made First. International journal of Engineering Technology, Management and Applied sciences, 5(3), pp. 2349-4476.

    8. Miskir Gebre Hiwot, P. T. Q. G. K., 2017. Comparative study on compressive strength of locally produced fired clay bricks and stabilized clay brick with cement and lime. Global Scientific Journals, 5(12), pp. 2320-9186.

    9. Nassif Nazeer Thaickavil, J. T., 2017. Bahaviour and strength assessment of Masonry prism. www.elsevier.com/locate/cscm, Issue 8, pp. 23-38.

1 thoughts on “Assessing the Effect of Different Mortar Mixes on Strength of Burnt Clay Brick Masonry Wall

  1. Owino Stephen says:

    I appreciate the comments given by colleagues and this type reviews make us better and impact better research results