Problem Analysis in Concrete Repair and Maintenance of Civil Engineering Structures

DOI : 10.17577/IJERTCONV5IS03027

Download Full-Text PDF Cite this Publication

Text Only Version

Problem Analysis in Concrete Repair and Maintenance of Civil Engineering Structures

Amit Singhal1,

1Department of Civil Engineering Department GITAM Kablana, India

Anshu3

Mamta2,

2Department of Civil Engineering Department GITAM Kablana, India

3Department of Civil Engineering Department GITAM Kablana, India

This study deals with experimental investigation for finding the causes of distressed concrete and their effects which reduces the load bearing capacity of the structures. The rehabilitation of existing reinforced cement concrete (RCC) bridges and building becomes necessary due to ageing, corrosion of steel reinforcement, defects in construction/design, demand in the increased service loads, and damage in case of seismic events and improvement in the design guidelines. Today, concrete repair is a major industry, supporting the need of virtually every concrete structure. Each structure requires routine repair and maintenance, ranging from simple protective coatings to repair of spalling concrete to strengthening of under-designed components. Developing effective repair strategies requires an understanding of what caused the undesirable behavior. Understanding the cause allows the repair strategy to address both the cause and the effect. The result is successful long lasting repair. The purpose of this study is to present concrete behavior under embedded metal corrosion, disintegration mechanisms, alkali-aggregate reaction (AAR), moisture effects, thermal effects, load effects and faulty workmanship.

Index Terms FRR, GFRP, AAR, RCC, C/D, ASTM,MMA.

  1. INTRODUCTION

    Sometimes in late 1970s, it finally was recognized that there was a major problem with the infrastructure in United States. In 1970s an alarm signal went off to let us know that more than 60% of our bridges were failing and need some form of repair. There was big uproar and considerable funds were pumped in to promote research and development in fixing them. The first Symposium (1981) on repair, rehabilitation and investigations [1], [2] was held in Mumbai as an attempt to bring talents from the west and east together to discuss the problem of universal nature. The deterioration of civil engineering infrastructures such as buildings, bridge decks, girders, offshore structures, parking structures are mainly due to ageing, poor maintenance, corrosion, exposure to harmful environments. These deteriorated structures cannot take the load for which they are designed. A large number of structures constructed in the past using the older design codes in different parts of the globe are structurally unsafe according to the new design codes and hence need up gradation. Using

    internally placed moving hinge, external post-tensioned straps, dowel shear devices, drilled hole shear transfer devices, grouted subgrade, cantilever shear arm, installing new expansion joint, section enlargement, shear collars, externally post tensioned reinforcement, bonded steel plates and concrete overlays we can strengthen and stabilized the different types of cracking in the reinforced cement concrete structures. The concrete jacketing also improves the load carrying capacity of the pile foundation of bridges. Portland cement mortar, Portland cement concrete, micro silica modified Portland cement concrete, latex modified Portland cement concrete, polymer modified Portland cement mortar with non-sag fillers, magnesium phosphate cement concrete, epoxy mortar, methylmethacrylate (MMA) [6] concrete and shot-crete may be used as repair and overlay materials.

  2. OBJECTIVE OF THE PRESENT WORK

    In the light of the literature survey presented above, the following objectives of are identified for the present work:

    1. To study the embedded metal corrosion in concrete structures.

    2. To study the disintegration mechanism of concrete structures.

    3. To investigate the effect of moisture in concrete.

    4. To study thermal effects in concrete structures.

    5. To study load effects in concrete structures.

    6. To study effect of faulty workmanship on concrete structures.

  3. TESTING METHODS FOR CONCRETE EVALUATION

    A thorough and logical evaluation of the current condition of the structure is the first step of any repair project. Concrete in a structure has a number of functions. Concrete is designed to carry loads. Disfunction [4], [5]of concrete structures usually occurs in some form of visible cracking, leaching, spalling, scaling, stains, disintegration, wear, settlement, or deflection. The evaluation of concrete structures can be either a reactive or proactive process. Concrete evaluation is not limited to studies of its physical conditions, mechanical properties, chemical make-up and external manifestation. Understanding its interaction with the environment is equally important. Any

    thorough investigation starts with a visual review of condition.

      1. Acoustic emission and thermography methods are used for locating delaminated concrete.

      2. Corrosion activity can be detected by placing a copper-copper sulfate half-cell and using a voltmeter.

      3. Chloride content in concrete can be calculated using chloride analyzer.

      4. To determine the depth of carbonation, a solution of phenolphthalein is sprayed over the surface of concrete.

      5. Petrographic [7] analysis is used to determine the formation and composition of concrete and to classify its type, condition and serviceability.

      6. Impact echo method is a reliable method of locating voids, cracks, honeycomb, and other flaws.

      7. Ultrasonic pulse velocity methods may be used to locate voids, cracks, and honeycomb.

      8. Fiber optics (borescope), video cameras, and periscopes are the tools that allow for remote viewing inside a structure. Remote viewing technique [10] requires larger drilled holes.

      9. The monitoring of cracks can be conducted with various tools including optical comparitors, glued glass strips, glued-in-place crack gauge, electrical transducers, and extensometers.

      10. One useful in situ test is pull-off test [11], which measures the bond between two layers.

      11. Rebound hammer method is used to measure the surface hardness of concrete.

    TABLE 1

    Standard Test Methods for Evaluating Concrete

    12

    AASHTO T 259

    Resistance of concrete to chloride ion penetration

    13

    AASHTO T 260

    Sampling and testing for total chloride ions in concrete

    14

    AASHTO T 277

    Rapid determination of the chloride permeability of concrete

    15

    ASTM C 457

    Microscopial determination of parameters of the air void system in hardened concrete

    16

    ASTM C 666

    Resistance of concrete to rapid freezing and thawing

    17

    ASTM C 671

    Critical dilation of concrete specimens subjected to freezing

    17

    ASTM C 671

    Critical dilation of concrete specimens subjected to freezing

  4. REPAIR MATERIALS AND PLACEMENT METHODS

    Different kinds of defect, repair methods and materials [13], [15], [18] are explained in the table below:

    TABLE 2

    tr>

    Defects

    Repair Methods

    Materials

    injection with flexible filler

    Elastromeric sealer Flexible epoxy filler Steel wire or rod

    Membrane or special mortar Steel plate, post tensioning, stitching, etc

    injection with rigid filler

    Cement grout or mortar, Fast-setting mortar. Rigid epoxy filler Bituminous coating, tar Asphalt overlay with membrane Latex modified concrete, highly dense concrete

    Dry-pack Mortar, Fast- setting mortar Cement mortar, Epoxy or Polymer concrete

    Steel rod Post tensioning, etc.

    Dry-pack Portland cement grout, mortar, cement Epoxy or Polymer concrete Fast-setting mortar

    Coarse aggregate and grout as needed

    Portland cement concrete, Latex modified concrete, Asphalt cement, Epoxy or polymer concrete

    Fast-setting mortar, Cement mortar

    Bituminous, Linseed oil coat, Silane treatment

    as needed

    • Live Cracks

    • Caulking

    • Pressure

    • Jacketing:

      • Strapping

      • Overlaying

    • Strengthening

    • Dormant Cracks

    • Caulking

    • Pressure

    • Coating

    • Overlying

    • Grinding and Overlay

    • Dry-pack

    • Shotcrete/Gunite

    • Patching

    • Jacketing

    • Strengthening

    • Reconstruction

    • Voids [10]

    • Hollows and

    • Honeycombs

    • Dry pack

    • Patching

    • Resurfacing

    • Shotcrete/Gunite

    • Preplaced aggregate

    • Replacement

    • Scaling Damage [14]

    • Overlaying

    • Grinding

    • Shotcrete/Gunite

    • Coating

    • Replacement

    Repair Materials and Placement Method

    S. No.

    Designation

    Title

    1

    ASTM C 42

    Obtaining and testing drilled [3], [12] cores and sawed beam of concrete

    2

    ASTM C 805

    Rebound number of hardened concrete

    3

    ASTM C 803

    Penetration resistance of hardened concrete [15]

    4

    ASTM C 597

    Pulse velocity through concrete

    5

    ASTM C 496

    Splitting tensile strength of cylindrical concrete [19]

    6

    ASTM C 78

    Flexural strength of concrete (with third-point loading)

    7

    ASTM C 293

    Flexural strength of concrete (with center-point loading)

    8

    ASTM C 418

    Abrasion resistance of concrete by sandblasting

    9

    ASTM C 876

    Half cell potentials of uncoated reinforcing steel in concrete

    10

    ASTM D 3633

    Electrical resistivity of Membrane- Pavement System

    11

    ASTM C 856

    Standard practice for petrographic examination of hardened concrete

    Concrete, Epoxy, Polymer, Latex, Asphalt Cement mortar, Fast-setting mortar Latex modified concrete, Asphalt concrete, Concrete Bituminous, linseed oil, Silane, etc. as needed

    • Spalling Damage [6], [7]

    • Patching

    • Shotcrete/Gunite

    • Overlay

    • Coating

    • Replacement

    4) With a cover-to-bar diameter ratio (C/D) of 7, concrete cracking starts when corrosion reaches 4 percent.

  5. CONCLUSION

    In this experimental investigation the causes and effects of undesirable behavior of concrete members are studied. The test results illustrated in the present study showed that the external strengthening with GFRP composites can be used to increase the shear capacity of RCC structures, but the efficiency varies depending on the test variables such as fiber orientations, wrapping schemes, number of layers and anchorage scheme.

    Based on the experimental and theoretical results, the following conclusions are drawn:

    1. The pH of newly produced concrete is usually between 12 and 13.

    2. In good quality concrete the corrosion rate will be very slow.

    3. Accelerated corrosion will take place if the pH is lowered [8], [9].

    Fig. 1 Embedded Metal Corrosion Process

    Fig. 2 Corrosion Induced Cracking and Spalling

    1. With a cover-to-bar diameter ratio (C/D) of 3, concrete cracking starts when corrosion reaches 1 percent.

    2. The research conducted on flexural beams found that in steel more than 1.5 percent corrosion, the ultimate load capacity began to fall, and at 4.5 percent corrosion, the ultimate load was reduced by 12 percent .

    3. It was demonstrated that a threshold level of 8000 ppm of chloride ions was required to initiate corrosion when the pH was 13.2 and when pH was lowered to11.6, corrosion was initiated with only 71 ppm of chloride ions.

    4. Carbonation will not occur when concrete is constantly under water .

    5. Normal weight concrete shrinks from 400 to 800 microstrains.

    6. A change of 38° C in a 30.5m length will change the overall length by 22mm.

    7. A precast double T-shaped structured member with a 18m span can move 19mm upward at midspan from normal diurnal solar heating, causing the ends to rotate and stress the ledger beam bearing pads and concrete.

    8. Hinges open and close with daily temperature changes.

    9. The cement mortar converts to quicklime at temperature of 400° C , thereby causing disintegration of the concrete.

    10. High slump mixes, incorrect methods of handling concrete, and over-vibration are the causes of segregation.

  6. FUTURE SCOPE

Perhaps in the years to come, we may be able to reduce the large expenses involved in repairs and rehabilitation of our structures and change the public image of our profession. Based on the finding and conclusions of the current study the following recommendations are made for future research in FRP shear strengthening:

  1. Strengthening of RCC bridges under IRC loading.

  2. Strengthening of existing residential building without interrupting residents.

  3. Strengthening of columns using jacketing same as in pile foundation.

  4. Strengthening of flexure member using external bonded steel plates at lower cost.

  5. To lower the final cost of repair of existing buildings.

  6. To improve the asthetic conditions of the bridges, T-beams and existing buildings.

  7. FRP strengthening of RC T-beams with different types of fibers such as carbon, aramid & basalt.

  8. Study of bond mechanism between CFRP, AFRP and BFRP and concrete substrate.

  9. Strengthening of RC L-beams with FRP composite.

  10. Strengthening of RC L-section beams with web opening.

  11. Effects of web openings of different shape and size on the shear behavior of T & L-beams.

  12. Effects of shear span to depth ratio on shear strengthening of beams.

  13. Numerical modelling of RC T & L-beams strengthened with FRP sheets anchored at the end.

REFERENCES

  1. Clifton, J.R, Predicting the Remaining Service Life of concrete, National Institute of Standards and technology Report NISTIR 4712.

  2. Bousselham A., and Chaallal O. (2006), Behaviour of Reinforced Concrete T-beams strengthened in shear with crbon fiber-reinforced polymer An Experimental Study,

    ACI Structural Journal, Vol. 103, No. 3, 339-347

  3. M.A. Shahawy, M. Arockiasamy, T. Beitelman, R. Sowrirajan Reinforced concrete rectangular beams strengthened with CFRP laminates Composites: Part B 27B (1996) 225-233

  4. Victor N. Kaliakin, Michael J. Chajes and Ted F. Januszka Analysis of concrete beams reinforced with externally bonded woven composite fabrics Composites: Part B 27B (1996) 235- 244

  5. Koji Takeda, Yoshiyuki Mitsui, Kiyoshi Murakami, Hiromichi Sakai and Moriyasu Nakamura Flexural behaviour of reinforced concrete beams strengthened with carbon fibre sheets Composites: Part A 27A (1996) 981-987

  6. Ahmed Khalifa, Antonio Nanni Improving shear capacity of existing RC T-section beams using CFRP composites Cement & Concrete Composites 22 (2000) 165-174

  7. Thanasis C. Triantafillou and Costas P. Antonopoulos Design of concrete flexural members strengthened in shear with FRP

    Journal of Composites for Construction, Vol. 4, No. 4,

    November, 2000. 198-205

  8. Hausmann, D. A, Steel Corrosion in Concrete Material Protection, November 1967, pp. 12-23.

  9. Sergio F. Brena, Regan M. Bramblett, Sharon L. Wood and Michael E. Kreger Increasing Flexural Capacity of Reinforced Concrete Beam Using Carbon Fiber Reinforced Polymer Composites ACI Structural Journal/January-February 2003. 36-46

  10. Bimal Babu Adhikary, Hiroshi Mutsuyoshi, and Muhammad Ashraf Shear Strengthening of Reinforced Concrete Beams Usmaing Fiber-Reinforced Polymer Sheets with Bonded Anchorage ACI Structural Journal/September-October 2004. 660-668

  11. Vaysburd, A. M., Sabnis, G. M and Sorokko, R., Theoretical Aspects and Testing Methods of Concrete Carbonation, Proceedings, International Conference on Life Prediction of Corrodible Structures, Hawaii, 1991, pp. 34/1-34/16

  12. American Concrete Institute, SP-102, Steel Corrosion in Concrete: Cause and Restraints, Detroit, 1987.

  13. ACI 201.2R-77, Guide to Durable Concrete.

  14. ACI 318-83, Corrosion of Metals in Concrete.

  15. Chloride Corrosion of Steel in Concrete, ASTM STP 627, American Society for Testing and Materials, Philadelphia, PA, 1977.

  16. Peter H. Emmons and Gajanan M. Sabnis, Concrete Repair and Maintenance, Galgotia Publication, 2012.

  17. L.J. Li, Y.C. Guo, F. Lui, J.H. Bungey An experimental and numerical study of the effect of thickness and length of CFRP on performance of repaired reinforced concrete beams

    Construction and Building Materials 20 (2006) 901-909

  18. Yung Chih Wang, Kai Hsu Design recommendations for the strengthening of reinforced concrete beams with externally bonded composites plates Composite Structures Articles in press. [16] IS: 456-2000, Plain and Reinforced Concrete Code of Practice, Bureau of Indian Standards.

  19. Al-Sulaimani, Kaleemullah, Basunbal and Rasheed , Influence of Corrosion and Cracking on Bond Behaviour and strength of Reinforced Concrete Members, ACI Structural Journal, March-April 1990, p220.