Experimental Investigation on Self Compacting Concrete by Replacing Industrial Waste Materials

Due to versatility of concrete as a construction material, it is utilized in large quantities over the world. Selfcompacting concrete is an innovative concrete which does not require any vibration and gets compacted on its own weight. To check the feasibility of utilizing different waste materials and industrial by products in concrete, extensive research has been carried out to develop high quality and grade of SCC. This paper reviews the influence of utilizing such waste materials as partial replacement of cement and the performance of SCC in both fresh and hardened state. Its durability aspects were also considered Keywords—Self compacting Concrete, Nano silica, Micro silica, Acid resistance, Sulphate resistance test, Acid resistance test. This Self-compacting concrete (SCC) was first developed in Japan (in the mid to late 1980s) as a means to create uniformity in the quality of concrete by controlling the ever present problem of insufficient compaction by a workforce that was losing skilled labor and by the increased complexity of designs and reinforcement details in modern structural members. Durability was the main concern and the purpose was to develop a concrete mix that would reduce or eliminate the need for vibration to achieve consolidation. Self-compacting concrete achieves this by its unique fresh state properties. In the plastic state, it flows under its own weight and maintain homogeneity while completely filling any formwork and passing around congested reinforcement. In the hardened state, it equals or excels standard concrete with respect to strength and durability. The use of SCC concrete has been increasing in the United States also during the last 5 years. Currently the technology is being primarily applied to the precast industry. Other segments being targeted are flatwork, columns and wall construction. The applications of SCC are many, limited only by the industry's knowledge of it, ability to produce it and acceptance of it. The usual selfcompacting concretes have compressive strengths in the range of 60-100N/mm2. However Ultra High Performance Self-Compacting Concrete (UHPSCC) with strength about 150N/mm2 has also been successfully developed. The durability of cement concrete is defined as its ability to resist weathering action, chemical attack, abrasion or any other process of deterioration. Durable concrete will remain its original form, quality and serviceability when exposed to its environment. I. LITERATURE REVIEW Ever since the first report of the development of SCC in Japan in 1988 by OZAWA ET AL using super plasticizers and viscosity against and in 1992, they again identified the factors controlling self-compacting namely coarse and fine aggregate content, and presented the paper at CANMET ACI International Conference (1992) which spread the concept of SCC in the world Ahamad Askari et.al (2011) An experimental investigation into mechanical properties of self-compacting concrete inculpating fly ash and silica fume at different ages of curing. Self-compacting mixtures had a cement replacement of 20, 30 and 40% with class F fly ash and 5,10 and 15% with silica fume. The results show that normal strength self-compacting concrete could be successfully produced using fly ash and silica fume. Compressive strength after 28 days in mixtures containing fly ash is fairly balanced, with the result that specimens containing 30% fly ash along with 5% silica fume content develop compressive strength similar to the control mixture. Mucteba Uysal et.al (2011) has investigated performance of self-compacting concrete containing different mineral admixtures. The influence of mineral admixture on a workability, compressive strength, ultrasonic pulse velocity, density and sulphate resistance of SCC was investigated. Sulphate resistance tests involved immersion in 10% magnesium sulphate and 10% sodium sulphate solutions for a period of 400 days. Replacing 25% of PC with FA resulted in strength of more than 150 Mpa at 400 days. On the other hand the best resistance to sodium and magnesium sulphate attacks was obtained from a combination of 40% GBFS (granulated blast furnace slag) with 60% PC. The pozzalanic materials FA and GBFS increased the late age compressive strength of SCC mixtures. Replacing 25% of PC with FA resulted in a strength of more than 150Mpa at 400 days. Replacing cement with 40% GBFS can reduce magnesium sulphate attack by one third when compared to control mixture. Kemalettin Yilmaz et.al (2011) has investigated effect of mineral admixtures on properties of self-compacting concrete Limestone powder (LP), Basalt powder (BP) and marble powder (MP) are used directly without attempting any additional processing in the production of SCC. The water to binder ratio is maintained at 30% for all mixtures. The results show that it is possible to successfully utilize waste LP, BP and MP as mineral admixtures in proceeding SCC. The addition of Limestone powder (LP), Basalt powder (BP) and International Journal of Engineering Research & Technology (IJERT) ISSN: 2278-0181 http://www.ijert.org IJERTV9IS050496 (This work is licensed under a Creative Commons Attribution 4.0 International License.) Published by : www.ijert.org Vol. 9 Issue 05, May-2020

This Self-compacting concrete (SCC) was first developed in Japan (in the mid to late 1980s) as a means to create uniformity in the quality of concrete by controlling the ever present problem of insufficient compaction by a workforce that was losing skilled labor and by the increased complexity of designs and reinforcement details in modern structural members. Durability was the main concern and the purpose was to develop a concrete mix that would reduce or eliminate the need for vibration to achieve consolidation. Self-compacting concrete achieves this by its unique fresh state properties. In the plastic state, it flows under its own weight and maintain homogeneity while completely filling any formwork and passing around congested reinforcement. In the hardened state, it equals or excels standard concrete with respect to strength and durability. The use of SCC concrete has been increasing in the United States also during the last 5 years. Currently the technology is being primarily applied to the precast industry. Other segments being targeted are flatwork, columns and wall construction. The applications of SCC are many, limited only by the industry's knowledge of it, ability to produce it and acceptance of it. The usual selfcompacting concretes have compressive strengths in the range of 60-100N/mm². However Ultra High Performance Self-Compacting Concrete (UHPSCC) with strength about 150N/mm² has also been successfully developed. The durability of cement concrete is defined as its ability to resist weathering action, chemical attack, abrasion or any other process of deterioration. Durable concrete will remain its original form, quality and serviceability when exposed to its environment.

I.
LITERATURE REVIEW Ever since the first report of the development of SCC in Japan in 1988 by OZAWA ET AL using super plasticizers and viscosity against and in 1992, they again identified the factors controlling self-compacting namely coarse and fine aggregate content, and presented the paper at CANMET ACI International Conference (1992) which spread the concept of SCC in the world Ahamad Askari et.al (2011) An experimental investigation into mechanical properties of self-compacting concrete inculpating fly ash and silica fume at different ages of curing. Self-compacting mixtures had a cement replacement of 20, 30 and 40% with class F fly ash and 5,10 and 15% with silica fume. The results show that normal strength self-compacting concrete could be successfully produced using fly ash and silica fume. Compressive strength after 28 days in mixtures containing fly ash is fairly balanced, with the result that specimens containing 30% fly ash along with 5% silica fume content develop compressive strength similar to the control mixture. Mucteba Uysal et.al (2011) has investigated performance of self-compacting concrete containing different mineral admixtures. The influence of mineral admixture on a workability, compressive strength, ultrasonic pulse velocity, density and sulphate resistance of SCC was investigated. Sulphate resistance tests involved immersion in 10% magnesium sulphate and 10% sodium sulphate solutions for a period of 400 days. Replacing 25% of PC with FA resulted in strength of more than 150 Mpa at 400 days. On the other hand the best resistance to sodium and magnesium sulphate attacks was obtained from a combination of 40% GBFS (granulated blast furnace slag) with 60% PC. The pozzalanic materials FA and GBFS increased the late age compressive strength of SCC mixtures. Replacing 25% of PC with FA resulted in a strength of more than 150Mpa at 400 days. Static and dynamic elastic moduli also increased and the higher static elastic modulus and dynamic elastic modulus have been obtained for MP20 and MP10. C.Selvamony et.al (2010) has investigation on self-compacted self-curing concrete using limestone powder and clinkers which the use of Silica fume in concrete increased the dosage of super plasticizers. At the same constant sp dosage 0.8% and mineral additive constant 30%, LP can better improve the workability than that of control and fine aggregate by 5% to 45%. A maximum of 8% of lime stone powder with silica fume, 30% of quarry dust and 14% of clinkers was able to be used as mineral admixtures without affecting the selfcompatibility. The silica fume was observed to improve the mechanical property of SCC, while limestone powder along with quarry dusts affecting mechanical properties of SCC. S.Venkateswara Rao et.al (2010) has investigation of effect of size of aggregate and fines on standard and high strength self-compacting concrete The mechanical properties viz., compressive strength, flexural strength and split tensile strengths were studied at the end of 3, 7 and 28 days for standard and high strength SCC with different sizes of aggregate. It was noted that with 10mm size aggregate and 52% fly ash in total powder the mechanical properties were superior in standard SCC, while 16 mm size aggregate with a 31% fly ash in total powder improved the properties of high strength SCC. Size of aggregate was 10mm for standard selfcompacting concrete (M30), while it is 16mm for high strength self-compacting concrete (M70) though all other sizes. Optimum dosages of fly ash were 52% addition in case of standard grade SCC and it is 31% addition in case of high strength SCC.
II. METHODOLOGY In this paper Self compacting concrete is made by replacing cement with Micro Silica and Nano silica. These materials were collected and replaced with Ordinary Portland Cement. Basic Physical, Mechanical properties and chemical compositions were tested for the mix design. Mix proportions were designed based on EFNARC guidelines. Fresh concrete and Workability tests were done for SCC as per code guidelines. In order to study about durability properties, few laboratory tests were done like Water absorption and Acid Resistance.

A. Portland Cement concrete
The Portland cement usually takes several hours to set, and will harden in a matter of weeks. Cement is a somewhat curious material in that it continues to harden over time as long as there is water available for the components of the cement to form bonds with. One week old Portland cement has strength of around 23 MPa, whereas three month old cement has a strength of 41 MPa. These numbers apply to standard Portland cement which has not had any additives added to it. Various treatments and additives can make cement set and harden at different rates, and various types of Portland cement also possess different properties which affect the rate of setting and hardening.

B. Aggregates
Crushed angular granite metal of 20 mm size from a local source was used as coarse aggregate. River sand was used as fine aggregate and was used in the investigation.

C. Superplasticizer
GLENIUM B233 consists of a carboxylic ether polymer with long side chains. At the beginning of the mixing process it initiates the same electrostatic dispersion mechanism as the traditional superplasticisers, but the side chains linked to the polymer backbone generates a steric hindrance which greatly stabilizes the cement particles ability to separate and disperse. Steric hindrance provides a physical barrier (alongside the electrostatic barrier) between the cement grains. With this process, flow able concrete with greatly reduced water content is obtained. The optimum dosage of SP should be determined with trial mixes.

D. Admixtues
The concrete mixtures investigated in this study were prepared with Portland cement type II, Micro silica powder and Nano silica. The specific gravity of micro silica and Nano silica is 2.17 and 1.03, and they are silica particles with a maximum size of 0.2 μm and 50 nm, respectively. In addition, Nano silica is a water emulsion with 50 % of dry solid and PH of 10.. The control mix which was exclude of micro silica and Nano silica  Using Nano silica in SCC individually there is no greater differences in strength gaining as compared to conventional concrete, but it as improve the flexural strength up to 5% using 3% of micro silica. The concrete with addition of 15% micro silica( based on the mass of cement) in SCC, the compressive strength, split tensile strength, flexural strength increased by 22%, 25%, 19% respectively.

B.HARDENED CONCRETE TEST RESULTS
The comparison results of micro silica, Nano silica, combination of micro silica and Nano silica specimen indicated that, a more suitable and strength gaining in SCC is combination of micro silica and Nano silica, that is concrete with combination of 15% of micro silica and 3% of Nano silica improve the compressive strength, split tensile strength, flexural strength by 25.61%, 25%, 19% respectively  The engineering properties of SCC such as Saturated Water absorption, Sulphate Resistance, Acid Resistance improved while designing 15% of micro silica with 3 % of Nano silica.

VII CONCLUSION
Based on experimental research for three selfcompacting concrete mixes (only micro silica, Nano silica, combination of micro and Nano silica), the following conclusions can be drawn at 28 days.
➢ Due to observed workability and high flow ability of SCC, it can be used in highly congested reinforcement structure as compare to conventional concrete.
➢ Using Nano silica in SCC individually there is no greater differences in strength gaining as compared to conventional concrete, but it as improve the flexural strength up to 5% using 3% of micro silica.
➢ 3.The concrete with addition of 15% micro silica( based on the mass of cement) in SCC, the compressive strength, split tensile strength, flexural strength increased by 22%, 25%, 19% respectively.
➢ AS a general conclusion, the comparison results of micro silica, Nano silica, combination of micro silica and Nano silica specimen indicated that, a more suitable and strength gaining in SCC is combination of micro silica and Nano silica, that is concrete with combination of 15% of micro silica and 3% Nano silica improve the compressive strength, split tensile strength, flexural strength by 25.61%, 25%, 19% respectively. ➢ 5.The engineering properties of SCC such as Saturated Water absorption , Sulphate Resistance , Acid Resistance improved while designing 15% of micro silica with 3 % of Nano silica.