Exploratory Study of Machine Crushed Over Burnt Brick as Coarse Aggregate in Concrete Hollow Blocks

DOI : 10.17577/IJERTV6IS020008

Download Full-Text PDF Cite this Publication

Text Only Version

Exploratory Study of Machine Crushed Over Burnt Brick as Coarse Aggregate in Concrete Hollow Blocks

Sajid Saleem

Department of Civil Engineering Surya World College of Engg. and Tech.

Rajpura, INDIA

Dr. Rajesh Goyal

Principal & professor Modern institute of Engg.&Tech.

Kurukshetra, India

Musawir Quadir

Department of Civil Engineering Ram Devi Jindal Faculty of Engg.&Tech.

Mohali, India.

AbstractThe main objective of the study is to explore and assess the possibility of using crushed over burnt brick aggregate (industrial waste) as an alternative for the costly conventional stone aggregate in concrete hollow blocks (masonry in fills) to reduce their production cost, construction cost, and in addition dead weight of a building structure. The study has been carried out at 0%,20%, 40%,60%,70%, 80% and 100% replacement levels of normal crushed stone aggregate with crushed over burnt brick aggregate by Arbitrary standards method. Cube specimens of sizes 150mm with different percentages by weight of normal stone aggregate to over burnt brick aggregate were casted and tested after 7 & 28 days. Whereas hollow block specimens of size 200×200×150mm were tested only after 28 days, as per IS standards. For the purpose of current study, batching operation by weight approach (Arbitrary standards method) has been adopted. Nominal mix of 1:8 (1 cement: 8 combined aggregates) or 1: 4: 4 has been investigated with water/cement ratio of 0.55. The constituents used in the mix were Portland pozzolana Cement (PPC) with 25% fly ash, fine aggregate (natural sand), coarse aggregates (locally available crushed stone aggregates 10 mm maximum size) and (crushed Over burnt brick aggregate of 10 mm maximum size), and potable water as per IS 456-2000.Comparative study among strengths of mixes, prepared at different replacement levels reveled that, crushed Over burnt brick aggregates can be confidently used upto 69% replacement level of normal crushed stone aggregate with crushed over burnt brick aggregate, with compromising with strength.

Keywords Cube, Hollow blocks, water cement ratio, aggregates, Compressive strength, burnt brick aggregate, concrete.

I. INTRODUCTION

Concrete hollow block is one of the most important developments in concrete masonry and it is widely used for both load bearing and non-load bearing masonry construction. It is made of cement and sand mix or concrete mix with dense or lightweight aggregates. It is an effective means of utilizing wastes generated by stone crushers, quarrying and stone processing units and other industries. The technology has high potential in areas where raw materials are easily available.

The Concrete Block Technology package is a highly profitable business for micro and small scale building material producers and construction companies.

  1. Appearance

    Concrete blocks have a light grey concrete colour, and on close inspection may show a granular texture depending on the type of aggregate used. Machine production provides even finish which offers savings on further cement plaster etc. Concrete blocks can be surface engineered by using pieces of stone or ceramic waste on their face.

  2. Thermal properties

    Concrete blocks have an excellent thermal property, comparable to other masonry units. The cavities in the blocks provide better thermal protection and also do not need external or internal plastering. The performance of these blocks increases with the increase in the number of hollow cores, which may or may not be filled in with some insulating materials.

  3. Sound insulation

    Concrete hollow blocks provide an acceptable degree of sound insulation. Insulation of concrete hollow blocks can further be improved by filling the cavities with an insulating material.

    1. MATERIALS USED

      1. over burnt brick aggregate.

        Over burnt brick aggregate can be considered as a good material suitable for plain concrete works as well as for reinforced works where stresses are not very high. Brick aggregate should be saturated with water before use to avoid absorption of the mixing water which is necessary for the hydration of cement and for the setting and hardening of the concrete. Brick aggregate is more fire resistant and sound absorbent than crushed stone aggregate.

        Fig.2.1 Typical shapes of Over Burnt Aggregate TABLE: 2.1 Properties of coarse aggregate.

        Properties

        Over burnt brick

        Normal stone

        Maximum

        10 mm

        10 mm

        Specific gravity

        1.75

        2.05

        Water absorption

        4.71

        1.00

        Bulk density

        1161.3

        1587.1

        Percentage void

        33.64

        22.58

        Aggregate

        35.75

        25.50

        Fineness modulus

        3.338

        3.407

        Fig: 2.2 particle size distribution curve of Over Burnt Aggregate

        Fig: 2.2 Aggregate crushing value of Over Burnt Aggregate

      2. Fine aggregate

        Natural sand conforming to Zone I with fineness modulus of

        3.016 has been used in the present study. The maximum size of sand was taken to be 4.75 mm. The testing of sand has been done as per IS-2386 (part I) 1963. Fineness modulus of sand =

          1. (Coarse sand)

            Fig 2.4 particle size distribution curve of fine aggregate

      3. Cement

        Portland Pozzolana cement conforming to Indian Standard: 1489(part I)-1991 has been used in the study. The various physical and mechanical properties investigated in the study are presented in table 2.2.

        TABLE 2.2: properties of cement

        Fineness (%)

        2.56

        Standard consistency (%)

        33

        Initial setting time (min.)

        192

        Final setting time (min.)

        273

        Average expansion (mm)

        0.75

        Compressive strength (N/mm²)

        3 day

        23.82

        7 day

        31.71

        28 day

        43.06

      4. Water

      Tap water, potable without any salts or chemicals was used in the study.

      Fig: 2.3 Aggregate crushing value of normal stone aggregate

    2. TEST PROGRAM

          • To explore and assess the possibility of using crushed Over burnt brick aggregate as an alternative for the normal crushed stone aggregate in concrete masonry unit (concrete hollow blocks) to reduce, the production cost of the unit, construction cost, and in addition, dead weight of a building structure.

          • To study the physical and mechanical properties of the over burnt brick aggregate concrete hollow block as per the specifications given by IS- codes of practice.

          • To carry out comparative study among strength, Economy.

    3. COMPRESSIVE STRENGTH TEST

      All batches described above in the experimental program were prepared, cured, and tested for compressive strength after 7 and 28 day. Standard 150 x 150 x 150 mm cubes & hollow block specimens of size 200×200×150mm cubes were used for compressive strength. hollow bloc specimens of size 200×200×150mm were tested only after 28 days. As shown in Figure 1, three identical specimens were crushed at 7 days and three identical specimens were crushed at 28 days. The compressive strength was calculated by dividing the failure load by average cross sectional area.

      Fig.3.1 concrete hollow blocks with Different percentage of OBA

      Fig.3.2 concrete cube specimens with and without replacement level

      Fig.3.3 test setup of cube specimen

      from the experimental observations, concrete hollow block with 60% over burnt brick aggregate gives the 28-day block strength of 1.87 n/mm2 the strength of over burnt brick aggregate concrete hollow block is inversely proportional to the percentage replacement of normal stone aggregate (p 1/rnormal stone aggregate).

      TABLE : 3.1 – Compressive strength test results for cube samples 150mm x 150mmx150mm & hollow block specimens of size 200×200×150mm

      Mix

      CUBE SAMPLES

      HOLLOW BLOCK

      Compressive strength N/mm²

      Average compressive strength N/mm²

      Compressi ve strength N/mm²

      Average compressive strength

      N/mm2

      7DAYS

      28 DAYS

      7 DAYS

      28 DAYS

      28 DAYS

      28DAYS

      0%

      9.83

      17.7

      9.74

      17.66

      3.96

      3.98

      9.74

      17.6

      4.06

      9.65

      17.69

      3.93

      20%

      8.71

      17.15

      8.82

      16.94

      3.63

      3.5

      8.80

      16.97

      3.40

      8.94

      16.71

      3.46

      40%

      7.91

      15.64

      7.86

      15.64

      3.03

      2.95

      7.73

      15.77

      2.90

      7.95

      15.51

      2.93

      60%

      7.51

      15.15

      7.33

      15.07

      1.93

      1.93

      7.15

      14.97

      1.80

      7.33

      15.11

      2.06

      70%

      7.06

      14.97

      7.12

      14.75

      1.60

      1.45

      7.15

      14.53

      1.40

      7.15

      14.75

      1.36

      80%

      7.02

      14.31

      6.84

      14.08

      1.10

      1.12

      6.80

      14.04

      1.20

      6.70

      13.91

      1.06

      100%

      6.31

      12.80

      6.18

      12.81

      0.86

      0.82

      6.17

      12.93

      0.83

      6.08

      12.71

      0.77

      se 2

      OBA

      ne2.5

      OBA

      ih 3

      4

      m/

      Fig.3.4 Comparison of 7 & 28 days compressive strength of cube specimens at different OBA levels.

      2 4.5

      m

      0% OBA

      N3.5

      n

      20%

      tg 40%

      rt 60%

      OBA

      70% OBA 80% OBA 100% OBA

      After 28days curing

      C 0

      o

      m0.5

      p

      er 1

      s

      vi 1.5

      Fig.3.5 Comparison of 28 days compressive strength of Hollow Block specimens at different OBA levels.

    4. CONCLUSIONS

In general, OVER BURNT BRICK AGGREGATE has good potential as coarse aggregate in the production of concrete hollow blocks. The following observations and conclusions can be made on the basis of the current study.

        • The crushing value of Over burnt brick aggregate is 10.25% higher than normal stone aggregate of 10mm maximum size but it is within the limits specified by IS codes of practice.

        • From the experimental observations, concrete hollow block with 60% over burnt brick aggregate gives the 28-day block strength of 1.87 n/mm2 and with 70% over burnt brick aggregate gives 1.44 n/mm². however, from the regression the required block

strength of 1.5n/mm² is attained at 69% inclusion of over burnt brick aggregate.

  • The percentage reduction in the production cost of the unit per month per factory at 69% replacement of normal stone aggregate by over burnt brick aggregate is 8.53% hence economical than normal concrete hollow block.

  • Besides achieving the above advantages, the suggested block also proves Eco-friendly as it utilizes the industrial waste which creates the large dumping problems.

REFERENCES

  1. Agrawal and KediaUses of fly ash in concrete hollow blocks.(1998)

  2. G.C.Singh.Building materials and construction(2000)

  3. M.S.Shetty;Concrete technology

  4. FadaCasi Geometric design of cores in concrete hollow Blocks for optimum weight(2004)

  5. Ganesen et al Influences of the type of block geometry on the behavior of hollowconcrete blocks.(1995)

  6. Hossain KMA, Uy BCharacteristics of volcanic ash and pumice based concrete(1999)

  7. Indian Standard: (part-I)-2003. Specification for Hollow and Solid concrete blocks.

  8. Indian Standard: (part-II)-1989. Specification for Hollow and Solid Light weightconcreteblocks.(2185)

  9. Indian Standard: 2386 (part-III)- .Methods of testing for coarse aggregatein concree.(1997)

  10. Indian Standard: 2386 (part-I and IV)Methods of testing for coarse aggregate inconcrete.(1997)

  11. Indian Standard: 383-Methods of testing for coarse aggregate in concrete.(1997)

  12. Indian standard: 1489 (part-I) Specifications for Portland pozzolana cement.

  13. Indian standard: 4031 (part-III and VI) Specifications for Portland pozzolana cement.

  14. Indian practical civil engineering hand book by Khanna P.N (2008)

  15. Kobbe, W.H, New uses forsulphur in industry, industrial and engineering chemistry.

  16. Melhotra N.A Investigations dealing with high volume fly ash concrete(1994)

  17. Meyer et alImprovement of thermal insulation of concrete hollow blocks by filling the cavities of blocks with heat-insulating material.(1999)

  18. Michael L. Whelan productivity improvements of concrete hollow block without losses in structural strength, system durability, or aesthetic appearance.(1992)

  19. M. Steadman et alInfluence of block geometry and grout type on compressive strength of block masonry.1999)

One thought on “Exploratory Study of Machine Crushed Over Burnt Brick as Coarse Aggregate in Concrete Hollow Blocks