Author(s): Ashish Haribhau Dawne, Prof. D. V. Pendam
Published in: International Journal of Engineering Research & Technology
License: This work is licensed under a Creative Commons Attribution 4.0 International License.
Volume/Issue: Volume. 6 - Issue. 06 , June - 2017
6060Al and Cu were joined by Friction stir welding process, and its effect on wear rate of the welded and non-welded zones of the joint were studied in this paper. Samples of 12mm in diameter were prepared from welded and non-welded zone for wear testing Pin-on-disc type machine (Model TR-20LE CHM-800, DUCOM) was used for dry sliding wear test in conformity to the ASTM G99 standard, for different loads of 10 and 15 Newton, keeping sliding distance constant. Wear behavior of welded and non-welded zones were determined for the joint and compared on Winducom 2010 software. The lowest wear rate was observed at the welded zone of the joint, whereas at non-welded zone (i.e. base metals) wear rate was more.
Number of Citations for this article: Data not Available
7 Paper(s) Found related to your topic:
Publish your Ph.D/Master's Thesis Online